Thermal conductivities of Zr-based transuranium nitride solid solutions
Zr含有超ウラン窒化物固溶体の熱伝導率
西 剛史; 高野 公秀; 市瀬 健一; 赤堀 光雄; 荒井 康夫
Nishi, Tsuyoshi; Takano, Masahide; Ichise, Kenichi; Akabori, Mitsuo; Arai, Yasuo
本研究では、2種類の(Zr,Pu,Am)Nと(Zr,Np,Pu,Am,Cm)N固溶体の焼結体試料を調製し、レーザフラッシュ法により熱拡散率を、ドロップカロリメトリにより比熱を測定し、熱伝導率を算出した。その結果、(Zr,Pu,Am)N及び(Zr,Np,Pu,Am,Cm)Nの熱伝導率は(Pu,Am)Nよりも熱伝導率が大きいこと,ZrNの熱伝導率は温度依存性が小さいものの、(Zr,Pu,Am)Nと(Zr,Np,Pu,Am,Cm)Nの熱伝導率は(Pu,Am)Nよりも温度とともに顕著に増加することが明らかとなった。
In this study, we prepared the sintered samples of two kinds of (Zr,Pu,Am)N and (Zr,Np,Pu,Am,Cm)N solid solutions. The thermal diffusivity and heat capacity of Zr-based transuranium nitride solid solutions were measured by a laser flash method and a drop calorimetry, respectively. The thermal conductivities of (Zr,Pu,Am)N and (Zr,Np,Pu,Am,Cm)N were determined from the measured thermal diffusivity, heat capacity and bulk density. It was found that the thermal conductivities of (Zr,Pu,Am)N and (Zr,Np,Pu,Am,Cm)N were higher than that of (Pu,Am)N. It was also found that the thermal conductivities of (Zr,Pu,Am)N and (Zr,Np,Pu,Am,Cm)N obviously increased with temperature in comparison with (Pu,Am)N, although they were smaller than that of ZrN over the temperature range investigated.
使用言語 : English
掲載資料名 : Journal of Nuclear Science and Technology
: 48
: 3
ページ数 : p.359 - 365
発行年月 : 2011/03
出版社名 : 日本原子力学会
特許データ :
PDF :
論文URL :
キーワード : no keyword
使用施設 :
広報プレスリリース :
論文解説記事
(成果普及情報誌)
: 燃料設計のためのデータベース構築に向けて; ZrN を希釈材としたTRU 窒化物固溶体の熱伝導率評価式の作成に成功[/]
受委託・共同研究相手機関 :
 
登録番号 : AA20100095
抄録集掲載番号 : 39000515
論文投稿番号 : 8738
Accesses  (From Jun. 2, 2014)
- Accesses
InCites™
パーセンタイル:29.93
分野:Nuclear Science & Technology
Altmetrics
Add This